cr12mov

cr12mov钢板  10*1800*6000 cr12mov模具钢

cr12mov钢板  12*1800*6000 cr12mov模具钢

cr12mov钢板  14*1800*6000 cr12mov模具钢

cr12mov钢板  15*1800*6000 cr12mov模具钢

cr12mov钢板  18*1800*6000 cr12mov模具钢

cr12mov钢板  20*1800*6000 cr12mov模具钢

cr12mov钢板  25*1800*6000 cr12mov模具钢

cr12mov钢板  30*1800*6000 cr12mov模具钢

cr12mov钢板  35*1800*6000 cr12mov模具钢

cr12mov钢板  38*1800*6000 cr12mov模具钢

cr12mov钢板  40*1800*6000 cr12mov模具钢

cr12mov钢板  45*1800*6000 cr12mov模具钢

cr12mov钢板  50*1800*6000 cr12mov模具钢

cr12mov钢板  55*1800*6000 cr12mov模具钢

cr12mov钢板  58*1800*6000 cr12mov模具钢

cr12mov钢板  65*1800*6000 cr12mov模具钢

cr12mov钢板  70*1800*6000 cr12mov模具钢

cr12mov钢板  75*1800*6000 cr12mov模具钢

cr12mov钢板  80*1800*6000 cr12mov模具钢

——————————

上海高高商贸有限公司：

电话：021-36308863

手机：18917081101

qq:404914802

阿里巴巴：shgaogaosu

联系人：粟太成

地址：上海市宝山区抚远路1288弄61号102室

————————————————————

牌号：cr12mov

材料名称：模具钢

标准：gb/t 1299-1985

材料的特性:

cr12mov模具钢的淬透性、淬火回火的硬度、耐磨性、强度均比cr12高。用于制造截面较大、形状复杂、工作条件繁重下的各种冷冲模具和工具，如冲孔凹模、切边模、滚边模、钢板cr12mov厚板深拉伸模、圆锯、标准工具和量规、螺纹滚模等。

化学成份:

碳 c ：1.45～1.70

硅 si：≤0.40

锰 mn：≤0.40

硫 s ：≤0.030

磷 p ：≤0.030

铬 cr：11.00～12.50

镍 ni：允许残余含量≤0.25

铜 cu：允许残余含量≤0.30

钒 v ：0.15～0.30

钼 mo：0.40～0.60

硬度:退火,255～207hb,压痕直径3.8～4.2mm;淬火,≥58hrc

热处理:

1)低淬低回： 淬火温度为950℃~1040℃，回火温度为200℃左右，二次回火

2)高淬高回： 淬火温度为1050~1100℃，回火温度为520℃左右，二次回火

高淬高回使用的了二次硬化法，从而提高硬度，但晶粒会长大。

为提高模具寿命达到80万模次以上，可对预硬钢实施淬火加低温回火的加硬方式来实现。淬火时先在500-600℃预热2-4小时，然后在850-880℃保温一定时间（至少2小时），放入油中冷却至50-100℃出油空冷，淬火后硬度可达50-52hrc，为防止开裂应立即进行200℃低温回火处理，回火后，硬度可保持48hrc以上回火。

cr12mov模具钢上海高高特钢将以真实信息、真格品质、真实价格的为您提供