c37100美标铅黄铜棒 易切削 化学成分

c37100 低铅黄铜棒

astm b981 c37100 astm b981/b981m introduction

应用：低铅黄铜棒、棒材和型材。

热处理：1954°c-1264°c。

astm b981 c37100 astm b981/b981m chemical

element min max similar

zn - - -

pb 1.5 2.5 -

other 99.5 - -

fe - 0.3 -

cu 58 61 -

astm b981 c37100 astm b981/b981m mechanical

yield tensile impact elongation reduction in cross section on fracture as-heat-treated condition brinell hardness (hbw)

rp0.2 (mpa) rm (mpa) kv/ku (j) a (％) z (％)

268 (≥) 941 (≥) 31 41 11 solution***aging, annealing, ausaging, q+t,etc 312

astm b981 c37100 astm b981/b981m physical

astm b981 c37100 astm b981/b981m的物理性能主要由电阻值模量、导热系数、比热容、热膨胀系数、弹性、泊松比、密度等表示。

temperature modulus of elasticity mean coefficient of thermal expansion 10-6/(°c) between 20(°c) and thermal conductivity specific thermal capacity specific electrical resistivity density poisson’s coefficient, ν

(°c) (gpa) (w/m·°c) (j/kg·°c) (ω mm2/m) (kg/dm3)

44 - - 0.14 -

166 594 - 33.3 434 -

727 - 43 34.2 421 444

astm b981 c37100 astm b981/b981m processing service

c37100易切削黄铜板材。c37100是一种易切削黄铜板材,具有优良的切削加工性能和良好的耐腐蚀性能,因此在机械制造、汽车、摩托车、电器、电子等领域得到广泛应用。

一、c37100易切削黄铜板材的力学性能

c37100易切削黄铜板材的抗拉强度、屈服强度、延伸率等力学性能均优于其他黄铜材料。其抗拉强度可达390mpa以上,屈服强度可达110mpa以上,延伸率可达30％以上。此外,c37100易切削黄铜板材还具有良好的冷加工性能和热加工性能,可满足不同加工工艺的要求。

二、c37100易切削黄铜板材的化学成分

c37100易切削黄铜板材的化学成分如下：

铜cu：58.0～62.0％

锌zn：余量

锡sn：≤0.2％

铝al：≤0.2％

铁fe：≤0.1％

铅pb：≤1.2％

砷as：≤0.02％

力学性能和化学成分是c37100易切削黄铜板材的重要指标,它们共同决定了材料的性能和使用范围。除了以上两个方面,还有其他一些因素 也需要考虑,例如材料的尺寸精度和表面质量等。这些因素 直接影响到产品的质量和生产效率。