zhpb65-2铸造铅黄铜棒
ys zhpb65-2 ys/t 544 introduction
用途：铸造铜合金锭。
热处理：1993°c-1592°c。
ys zhpb65-2 ys/t 544 chemical
for ys zhpb65-2 ys/t 544 datasheet***ys zhpb65-2 ys/t 544 chemical composition, please see the table below.
element min max similar
si - 0.03 -
p - 0.02 -
al - 0.1 -
sn - 1.5 -
mn - 0.2 -
fe - 0.7 -
zn - - -
pb 1 2.8 -
cu 63 66 -
ys zhpb65-2 ys/t 544 mechanical
yield tensile impact elongation reduction in cross section on fracture as-heat-treated condition brinell hardness (hbw)
rp0.2 (mpa) rm (mpa) kv/ku (j) a (％) z (％)
221 (≥) 959 (≥) 44 24 22 solution***aging, annealing, ausaging, q+t,etc 242
ys zhpb65-2 ys/t 544 physical
ys zhpb65-2 ys/t 544的物理性能参数主要由ys zhpb65-2 ys/t544的导热系数、比热容、弹性模量、热膨胀系数、电阻值、密度、泊松比等参数表示。
temperature modulus of elasticity mean coefficient of thermal expansion 10-6/(°c) between 20(°c) and thermal conductivity specific thermal capacity specific electrical resistivity density poisson’s coefficient, ν
(°c) (gpa) (w/m·°c) (j/kg·°c) (ω mm2/m) (kg/dm3)
42 - - 0.33 -
684 468 - 42.3 313 -
379 - 11 31.2 322 321
ys zhpb65-2 ys/t 544 processing service
zhpb65-2铸造铅黄铜棒是一种铜合金,具有优良的铸造性能、切削加工性能和抗腐蚀性能。它广泛应用于船舶、汽车、建筑、管道等领域,用于制造各种零部件和结构件。
这种铸造铅黄铜棒的成分中,铜和铅是主要的合金元素 。铜赋予了合金良好的强度和延展性,而铅则有助于改善铸造性能和切削加工性能。此外,锌和锡等元素 也常被添加到这种合金中,以进一步提高其强度和耐腐蚀性能。
zhpb65-2铸造铅黄铜棒的制造过程主要包括熔炼、浇注、冷却和精整等步骤。在熔炼过程中,铜和铅等原材料被加热到高温状态并充分熔化,以确保合金的成分均匀。浇注时将熔融的合金注入模具中,冷却后得到所需的形状和尺寸。最后进行精整,以去除表面缺陷和修整尺寸。
这种铸造铅黄铜棒具有许多优点,例如优良的铸造性能、切削加工性能和抗腐蚀性能。此外,它还具有良好的导热性和耐疲劳性能,使其适用于制造需要承受高负荷和高温的零部件。
总之,zhpb65-2铸造铅黄铜棒是一种广泛应用于船舶、汽车、建筑、管道等领域的优质铜合金材料