牌号 | cw401j铜镍锌合金 锌白铜线材 | ||||||
欧标钢号 | cuni10zn27 | ||||||
对应标准 | en 12166-1998 | ||||||
铜和铜合金:一般铜线材 | |||||||
归类 | 铜及铜合金 | ||||||
标签 | 铜镍锌合金 锌白铜 | ||||||
密度 | 8.6 g/cm3 | ||||||
cw401j化学元素 成分含量(%) | |||||||
成分 | fe | mn | ni | cu | pb | 其他合计 | 更多 |
最 小值 | - | - | 9 | 61 | - | - | zn:余量 |
最 大 值 | 0.3 | 0.5 | 11 | 64 | 0.05 | 0.2 | |
其他单个或其他合计化学成分包括表中未值的化学成分。只有在假定存在或在常规分析中,且有迹象表明其成分将超过规定值的情况下,才应进行分析。 | |||||||
cw401j机械性能 | |||||||
直径③ | 标记 | 热处理或状态 | 抗拉强度 | 屈服点 | 断后伸长率或延伸率 | 硬度 | |
d | σb | σs | δ | hbw | |||
mm | mpa | mpa | % | ||||
0.1≤d≤0.5 | cuni10zn27-r430 | 软;r430 | 430~530 | ≈190* | ≥20*(a100) | ||
0.5 |
cuni10zn27-r400 | 软;r400 | 400~510 | ≈180* | ≥25(a100) | ||
1.5 |
cuni10zn27-r370 | 软;r370 | 370~480 | ≈170* | ≥30(a100) | ||
1.5≤d≤4 | cuni10zn27-h085 | 软;h085 | hv: 85~140 | ||||
4 |
cuni10zn27-r360 | 软;r360 | 360~480 | ≈160* | ≥35(a11.3); | ||
≥40(a) | |||||||
4 |
cuni10zn27-h080 | 软;h080 | hv: 80~130 | ||||
0.1≤d≤0.5 | cuni10zn27-r520 | 1/4硬;r520 | 520~620 | ≈340* | ≥5*(a100) | ||
0.5 |
cuni10zn27-r480 | 1/4硬;r480 | 480~580 | ≈320* | ≥8*(a100) | ||
1.5 |
cuni10zn27-r460 | 1/4硬;r460 | 460~560 | ≈310* | ≥12*(a100) | ||
4 |
cuni10zn27-r440 | 1/4硬;r440 | 440~540 | ≈290* | ≥15*(a11.3); | ||
≥20*(a) | |||||||
1.5≤d≤20 | cuni10zn27-h130 | 1/4硬;h130 | hv: 130~170 | ||||
0.1≤d≤0.5 | cuni10zn27-r620 | 1/2硬;r620 | 620~730 | ≈510* | |||
0.5 |
cuni10zn27-r580 | 1/2硬;r580 | 580~680 | ≈470* | |||
1.5 |
cuni10zn27-r560 | 1/2硬;r560 | 560~660 | ≈460* | ≥5*(a100) | ||
1.5≤d≤4 | cuni10zn27-h170 | 1/2硬;h170 | hv: 170~200 | ||||
4 |
cuni10zn27-r530 | 1/2硬;r530 | 530~630 | ≈440* | ≥6*(a11.3) | ||
4 |
cuni10zn27-h165 | 1/2硬;h165 | hv: 165~195 | ||||
0.1≤d≤0.5 | cuni10zn27-r730 | 韧硬;r730 | 730~850 | ≈710* | |||
0.5 |
cuni10zn27-r680 | 韧硬;r680 | 680~800 | ≈670* | |||
1.5 |
cuni10zn27-r660 | 韧硬;r660 | 660~780 | ≈650* | |||
1.5≤d≤4 | cuni10zn27-h195 | 硬;h195 | hv: 195~225 | ||||
4 |
cuni10zn27-r630 | 硬;r630 | 630~750 | ≈620* | |||
4 |
cuni10zn27-h185 | 硬;h185 | hv: 185~215 | ||||
0.1≤d≤0.5 | cuni10zn27-r850 | 韧硬;r850 | ≥850 | ≈860* | |||
0.5 |
cuni10zn27-r800 | 韧硬;r800 | ≥800 | ≈810* | |||
1.5 |
cuni10zn27-r780 | 韧硬;r780 | ≥780 | ≈790* | |||
1.5≤d≤4 | cuni10zn27-h210 | 韧硬;h210 | hv: ≥210 | ||||
所有规格 | cuni10zn27-m | m | 不作规定 | 不作规定 | 不作规定 | 不作规定 | |
①材料状态名称及字符代号:h-硬度(布氏硬度或维氏硬度),后缀数字表示硬度值;r-抗拉强度,后缀数字表示最 小抗拉强度值;m-制造时,没有的机械性能。参见标准en 1173-2008 | |||||||
②a100、a11.3、a-标距 | |||||||
③或多边形线材的等效截面积 | |||||||
*这些数据不是本标准的要求,仅供参考 |