工业:耐腐蚀/耐压铸件、高速/重承、叶轮、泵
chemical composition
cu%1
pb%
sn%
zn%
fe%
p
ni%2
al%
bi%
s%
sb%
si%
|
|||||||||||
87.00- 91.00 |
0.10 |
2.70- 3.70 |
2.00- 4.00 |
0.30 |
0.05 |
1.00 |
0.005 |
2.70- 3.70 |
0.08 |
0.25 |
0.005 |
c89831 | 85 | 0.318 |
29 | 200 | 13 | 90 | 5 | 55 |
physical properties provided by cda
|
|||||||||||
melting point - liquidus | 1893 °f | 1033 °c | |||||||||
melting point - solidus | 1518 °f | 825 °c | |||||||||
density | 0.318 lb/in3 at 68 °f | 8.81 gm/cm3 at 20 °c | |||||||||
specific gravity | 8.81 | 8.81 | |||||||||
electrical conductivity | 20.38% iacs at 68 °f | 0.117 megasiemens/cm at 20 °c | |||||||||
thermal conductivity | 50 btu/sq ft/ft hr/°f at 68 °f | 86.6 w/m at 20 °c | |||||||||
coefficient of thermal expansion 68-392 | 10 · 10-6 per °f (68-392 °f) | 17.3 · 10-6 per °c (20-200 °c) | |||||||||
specific heat capacity | 0.092 btu/lb/°f at 68 °f | 385.4 j/kg at 20 °c | |||||||||
modulus of elasticity in tension | 13700 ksi | 94458 mpa |