pa66 45hsb nc010 高粘度,热稳定,注塑和挤出级
zytel® 45hsb nc010 | pa66 nylon resin
regional availability
north america, asia pacific, south【敏感词】central america
processing
injection moulding, film extrusion, profile extrusion, sheet extrusion, other extrusion, coatable, casting
delivery form
pellets
special characteristics
heat stabilised【敏感词】stable to heat
product text
common features of zytel® nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical and flammability properties, good abrasion【敏感词】chemical resistance. in addition, zytel® nylon resins are available in different modified【敏感词】reinforced grades to create a wide range of products with tailored properties for specific processes【敏感词】end-uses. zytel® nylon resin, including most flame retardant grades, offer the ability to be coloured.
the good melt stability of zytel® nylon resin normally enables the recycling of properly handled production waste. if recycling is not possible, dupont recommends, as the preferred option, incineration with energy recovery (-31kj/g of base polymer) in appropriately equipped installations. for disposal, local regulations have to be observed.
zytel® nylon resin typically is used in demanding applications in the automotive, furniture, domestic appliances, sporting goods and construction industry.
zytel® 45hsb is a high viscosity, heat stabilised polyamide 66 resin for injection moulding【敏感词】extrusion.
profile extrusion
preprocessing
drying recommended = yes, if moisture content of resin exceeds recommended level
drying temperature = 80℃
drying time, dehumidified dryer = 4-6 h
processing moisture content = <0.05 %
processing
melt temperature optimum = 285℃
melt temperature range = 280-290℃
properties
rheological properties |
dry / cond |
unit |
test standard |
moulding shrinkage,parallel |
1.4 / * |
% |
iso 294-4,2577 |
moulding shrinkage,normal |
1.4 / * |
% |
iso 294-4,2577 |
mechanical properties |
dry / cond |
unit |
test standard |
tensile modulus |
3100 / 1300 |
mpa |
iso 527-1/-2 |
yield stress |
83 / 55 |
mpa |
iso 527-1/-2 |
yield strain |
4 / 25 |
% |
iso 527-1/-2 |
nominal strain at break |
>50 / >50 |
% |
iso 527-1/-2 |
charpy notched impact strength,23℃ |
6 / 20 |
kj/m2 |
iso 179/1ea |
charpy notched impact strength,-30℃ |
5.5 / 4 |
kj/m2 |
iso 179/1ea |
thermal properties |
dry / cond |
unit |
test standard |
melting temperature,10℃/min |
262 / * |
℃ |
iso 11357-1/-3 |
temp. of deflection under load,1.8 mpa |
70 / * |
℃ |
iso 75-1/-2 |
coeff. of linear therm. expansion,parallel |
100 / * |
e-6/k |
iso 11359-1/-2 |
coeff. of linear therm. expansion,normal |
100 / * |
e-6/k |
iso 11359-1/-2 |
flammability |
dry / cond |
unit |
test standard |
burning behav. at 1.5 mm nom. thickn. |
hb / * |
class |
iec 60695-11-10 |
thickness tested |
1.5 / * |
mm |
iec 60695-11-10 |
ul recognition |
ul / * |
- |
- |
burning behav. at thickness h |
hb / * |
class |
iec 60695-11-10 |
thickness tested |
0.7 / * |
mm |
iec 60695-11-10 |
electrical properties |
dry / cond |
unit |
test standard |
comparative tracking index |
600 / - |
- |
iec 60112 |
other properties |
dry / cond |
unit |
test standard |
density |
1140 / - |
kg/m3 |
iso 1183 |
material specific properties |
dry / cond |
unit |
test standard |
viscosity number |
290 / * |
cm3/g |
iso 307,1157,1628 |
rheological calc. properties |
value |
unit |
test standard |
min. mould temperature |
50 |
℃ |
- |
min. melt temperature |
280 |
℃ |
- |
chemical media resistance
acids
√ acetic acid (5% by mass) (23℃)
√ citric acid solution (10% by mass) (23℃)
√ lactic acid (10% by mass) (23℃)
× hydrochloric acid (36% by mass) (23℃)
× nitric acid (40% by mass) (23℃)
× sulfuric acid (38% by mass) (23℃)
× sulfuric acid (5% by mass) (23℃)
× chromic acid solution (40% by mass) (23℃)
bases
× sodium hydroxide solution (35% by mass) (23℃)
√ sodium hydroxide solution (1% by mass) (23℃)
√ ammonium hydroxide solution (10% by mass) (23℃)
alcohols
√ isopropyl alcohol (23℃)
√ methanol (23℃)
√ ethanol (23℃)
hydrocarbons
√ n-hexane (23℃)
√ toluene (23℃)
√ iso-octane (23℃)
ketones
√ acetone (23℃)
ethers
√ diethyl ether (23℃)
mineral oils
√ sae 10w40 multigrade motor oil (23℃)
× sae 10w40 multigrade motor oil (130℃)
× sae 80/90 hypoid-gear oil (130℃)
√ insulating oil (23℃)
standard fuels
√ iso 1817 liquid 1 (60℃)
√ iso 1817 liquid 2 (60℃)
√ iso 1817 liquid 3 (60℃)
√ iso 1817 liquid 4 (60℃)
√ standard fuel without alcohol (pref. iso 1817 liquid c) (23℃)
√ standard fuel with alcohol (pref. iso 1817 liquid 4) (23℃)
√ diesel fuel (pref. iso 1817 liquid f) (23℃)
√ diesel fuel (pref. iso 1817 liquid f) (90℃)
× diesel fuel (pref. iso 1817 liquid f) (>90℃)
salt solutions
√ sodium chloride solution (10% by mass) (23℃)
× sodium hypochlorite solution (10% by mass) (23℃)
√ sodium carbonate solution (20% by mass) (23℃)
√ sodium carbonate solution (2% by mass) (23℃)
× zinc chloride solution (50% by mass) (23℃)
other
√ ethyl acetate (23℃)
× hydrogen peroxide (23℃)
× dot no. 4 brake fluid (130℃)
× ethylene glycol (50% by mass) in water (108℃)
√ 1% nonylphenoxy-polyethyleneoxy ethanol in water (23℃)
√ 50% oleic acid + 50% olive oil (23℃)
√ water (23℃)
× water (90℃)
× phenol solution (5% by mass) (23℃)
symbols used:
√ possibly resistant
defined as: supplier has sufficient indication that contact with chemical can be potentially accepted under the intended use conditions【敏感词】expected service life. criteria for assessment have to be indicated (e.g. surface aspect, volume change, property change).
× not recommended - see explanation
defined as: not recommended for general use. however, short-term exposure under certain restricted conditions could be acceptable (e.g. fast cleaning with thorough rinsing, spills, wiping, vapor exposure).